| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 305 - 310 |
| Density | g mL-1 | 2.15 |
| Coefficient of Thermal Expansion | cm / (cm °C) | |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity x 10-5 | W / mK | |
| Rockwell Hardness, D Scale | n/a | D56 - D60 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 14.5 - 16 |
| Tensile Strength, Break at 23 C | MPa | 25 - 35 |
| Elongation, Yield | % | 350 |
| Elongation, Break | % | 380 |
| Tensile Modulus at 23 C | MPa | 435 - 530 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | 520 - 690 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | |
| Izod Unnotched | J / m | No Break |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 7.5 | |
| Dielectric Constant @ 1 MHz | n/a | 2.02 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 1.9 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 260 | |
| Water Absorption, 24 hr. Immersion | % | 0.018 - 0.03 |